● High efficiency
● Low threshold
● Good anti-UV irradiation property
● Good thermal stability
● Good repetition rate
Host | Yttrium Aluminium Garnet (Y3Al5O12) |
Dopant | Nd3+, Ce3+ |
Concentration | 0.6~2.5% , ±0.1% |
Growth Direction of Crystal | [111] |
Wavefront Distortion | λ/8 per inch @632.8nm |
Extinction Ratio | ≧30dB |
Dimensions | Diameter: 2~30mm , Length: 0.3~120mm |
Tolerances | Diameter±0.02mm, Length±0.2mm |
Barrel Surface | Fine ground, Polished or Grooved |
Parallelism | ≤10″ |
Perpendicularity | ≤5’ |
Surface Flatness | λ/10 per inch @632.8nm |
Surface Quality | 10-5(MIL-PRF-13830B) |
Chamfer | 0.1mm@45° |
Clear Aperture | >95% |
Anti-Reflection Coating | R<0.15%@1064nm |
High-Reflection Coating | Standard HR Coating with R>99.8%@1064nm |
Damage Threshold | >750MW/cm2 |
Note: Parameters above can be customized as required. |